PBT it is one of the advanced engineering plastics with high rigidity, high toughness, good fatigue resistance, weather resistance, low water absorption rate (all the properties maintain under moisture atmosphere including electrical properties), high dielectric ability, good electrical capacity, size stability, good formability, excellent anti-creep ability under high impact, and good chemical properties as well. It is easy to process into glass-fiber reinforced and flame-retardant products. PBT/PET can be ultrasonic welded and easily post-processed.
¡ñHigh toughness, high modulus, low creep
¡ñGood dielectric strength
¡ñGood dimensional stability
¡ñLow water absorption rate, good hydrolysis resistance
¡ñGood heat resistance, low coefficient of thermal expansion
¡ñHigh impact strength
¡ñResistance to Thermal aging
¡ñEasy to process
|
PBT 605
Flame-retardant Polybutylene Terephthalate
|
|
Characteristics
|
Meet the environmental standards of RoHS and IEC, high gloss, UL94 V-0 flame retardant,good light shading and ageing resistance.
|
|
Applications
|
Plug in fluorescent light, electrical equipment shell, etc.
|
|
Properties (23¡æ)
|
Typical Value[1]
|
Unit
|
Test Method
|
|
Mechanical
|
|
Tensile Stress
|
52
|
MPa
|
ISO 527
|
|
Tensile Strain
|
8
|
%
|
ISO 527
|
|
Flexural Stress
|
88
|
MPa
|
ISO 178
|
|
Flexural Modulus
|
3000
|
MPa
|
ISO 178
|
|
Izod Impact Strength
(Notched)
|
6
|
kJ/m2
|
ISO 180
|
|
Other
|
|
Density
|
1.47
|
g/cm3
|
ISO 1183
|
|
Volume Resistivity
|
1E14
|
Ohms¡¤cm
|
IEC 60093
|
|
Flammability
|
V-0
|
Class
|
UL-94
|
|
Whiteness
|
95
|
-
|
-
|
|
Mold Shrinkage
|
1.5-1.9
|
%
|
ISO 294
|
|
Molding Process[2]
|
|
Drying Condition
|
Temperature
|
120-140¡æ
|
|
Time
|
2-4h
|
|
Mold Temperature
|
120¡æ
|
|
Barrel Temperature
|
Nozzle
|
Front
|
Middle
|
Rear
|
|
240-260 ¡æ
|
230-260 ¡æ
|
230-250 ¡æ
|
220-240 ¡æ
|
|
Note£º
[1] These figures are only intended as a guide and should not be used in preparing specifications.
[2] The molding process is only for reference and can be adjusted according to different models and products.
|